Bond strength to ZLS ceramics at different etching times and cementation protocols after aging

Authors

DOI:

https://doi.org/10.14295/bds.2019.v22i4.1816

Abstract

Objective: To assess the influence of 5% hydrofluoric acid etching time (ET), cementation protocol (CP), and thermal cycling (TC) aging on the microshear bond strength (µSBS) of zirconia-reinforced lithium silicate ceramic (ZLS) to adhesive resin cement. Material and Methods: Ten VITA Suprinity® ceramic blocks were cut in 120 slices (1.4 mm thickness) and randomly assigned to 12 groups (n = 10) according to the combination of factors (2x3x2 design): etching time (20 or 30 s), cementation protocol (silane + universal adhesive + resin cement; universal adhesive + resin cement; silane + resin cement) and thermal cycling (cycled or no-cycled). RelyX Ceramic Primer and Scotchbond™ Universal Adhesive were used respectively as silane (S) and universal adhesive (Ua). Ceramic surface was etched, and the cementation protocol performed on the delimited bonding area. Then, resin cement (RelyX™ Ultimate Cement [Rc]) cylinders were bonded and light cured. After, specimens were stored in deionized water at 37°C for 7 days and subjected to the µSBS test. Results: Data passed the normality test and three-way ANOVA analysis showed statistical difference (p<0.01) for isolated; double (ET/TC) (p<0.05), and triple (p<0.05) factor interactions. Conclusion: The combination 30s etching-Ua-Rc presented higher adhesive bond strength after thermal aging.

Downloads

Published

2019-10-31

Issue

Section

Clinical or Laboratorial Research Manuscript