The The Effect of GaAlAs Laser, Sandblasting, and Primers on Bond Strength between Zirconia Ceramic and Direct Resin Composite after Thermocycling
Bonding zirconia ceramic with resin composite
DOI:
https://doi.org/10.14295/bds.2021.v24i3.2534Abstract
Objective: This study was conducted to evaluate the shear bond strength (SBS) of resin composite on zirconia ceramic after different surface treatments and thermocycling. Material and Methods: Two hundred and seven zirconia specimens were divided into 9 groups and treated as follows: Group C-no treatment (served as the control); Group PC-Clearfil Ceramic primer (CP); Group PZ-Z-Prime Plus primer (ZP); Group A-sandblasted with 50 µm Al2O3 at 0.25 MPa for 20 s at a distance of 10 mm; Group AC-sandblasted and coated with CP; Group AZ-sandblasted and coated with ZP; Group L-GaAlAs diode laser with 808±5 mm wavelength, 3 watts power, and 10 Hz frequency; Group LC-GaAlAs diode laser coated with CP; and Group LZ-GaAlAs diode laser coated with ZP. All specimens were directly bonded with a resin composite cylinder using Adper Scotchbond Multi-purpose. Specimens were stored at 37ºC for 30 days and subjected to 2,500 thermocycles from 5ºC and 55ºC before the SBS was performed. One-way ANOVA and Tukey’s HSD test (=0.05) were performed. Surface topography changes were evaluated with a scanning electron microscope (SEM). Results: Sandblasting combined with CP or ZP (25.08±0.86 and 24.78±0.13 MPa, respectively) yielded the highest SBS and was significantly different from other methods (p<0.05). SEM showed various degrees of changes depending on different surface treatments. Conclusion: Surface treatment by sandblasting combined with a CP or ZP significantly provide the highest SBS between zirconia and resin composite.
KEYWORDS
Bond strength; Resin composite; Surface treatment; Zirconia ceramic.
References
Gautam C, Joyner J, Gautam A, Rao J, Vajtai R. Zirconia based dental ceramics: structure, mechanical properties, biocompatibility and applications. Dalton Trans 2016 Dec;45(48):19194-215. doi: 10.1039/C6DT03484E.
Agingu C, Zhang CY, Jiang NW, Cheng H, Özcan M, Yu H. Intraoral repair of chipped or fractured veneered zirconia crowns and fixed dental prosthesis: clinical guidelines based on literature review. J Adh Sci Tech 2018 Feb;32(15):1711-23. doi: 10.1080/01694243.2018.1443639.
Schley J, Heussen N, Reich S, Fischer J, Haselhuhn K, Wolfart S, et al. Survival probability of zirconia-based fixed dental prostheses up to 5 yr: a systematic review of the literature. Eur J Oral Sci 2010 Oct;118(5):443-50. doi: 10.1111/j.1600-0722.2010.00767.x.
Stangel I, Nathanson D, Hsu CS. Shear strength of the composite bond to etched porcelain. J Dent Res 1987 Sep;66(9):1460-5. doi: 10.1177/00220345870660091001.
Yun JY, Ha SR, Lee JB, Kim SH. Effect of sandblasting and various metal primers on the shear bond strength of resin cement to Y-TZP ceramic. Dent Mater 2010 Jun;26(11):650-8. doi: 10.1016/j.dental.2010.03.008.
Khan AA, Al Kheraif AA, Jamaluddin S, Elsharawy M, Divakar DD. Recent trends in surface treatment methods for bonding composite cement to zirconia: a reveiw. J Adhes Dent 2017 Jan;19(1):7-19. doi: 10.3290/j.jad.a37720.
Nagaoka N, Yoshihara K, Tamada Y, Yoshida Y, Meerbeek BV. Ultrastructure and bonding properties of tribochemical silica-coated zirconia. Dent Mater J. 2019 Feb;38(1):107-13. doi: 10.4012/dmj.2017-397.
Kasraei S, Atefat M, Beheshti M, Safavi N, Mojtahedi M, Rezaei-Soufi L . Effect of surface treatment with carbon dioxide (CO2) laser on bond strength between cement resin and zirconia. J Lasers Med Sci 2014 Summer;5(3):115-20. doi: 10.22037/jlms.v5i3.6438.
Usumez A, Hamdemirci N, Koroglu BY, Simsek I, Parlar O, Sari T. Bond strength of resin cement to zirconia ceramic with different surface treatments. Lasers Med Sci 2013 Jan;28(1):259-66. doi: 10.1007/s10103-012-1136-x.
Sofi LR, Fekrazad R, Akbarzadeh M, Maleki M. Effect of Er: YAG Laser, sandblast and several types of universal bonding on shear bond strength of zirconia ceramic to composite resin. J Contemp Dent Pract 2018 Oct;19(10):1246-53. doi: 10.5005/JP-JOURNALS-10024-2412.
Tokar E, Polat S, Ozturk C. Repair bond strength of composite to Er,Cr:YSGG laser irradiated zirconia and porcelain surfaces. Biomed J 2019 Jun;42(3):193-9. doi: 10.1016/j.bj.2019.02.001.
Stubinger S, Homann F, Etter C, Miskiewicz M, Wieland M, Sader R. Effect of Er:YAG, CO2 and diode laser irradiation on surface properties of zirconia endosseous dental implants. Lasers Surg Med 2008 Mar;40(3):223-8. doi: 10.1002/lsm.20614.
Kushima SS, Nagasawa M, Shibli JA, Brugnera A Jr, Rodrigues JA, Cassoni A. Evaluation of temperature and roughness alteration of diode laser irradiation of zirconia and titanium for peri-implantitis treatment. Photomed Laser Surg 2016 May;34(5):194-9. doi: 10.1089/pho.2015.4026.
Kriebel M. Effect of Er,Cr: YSGG and diode laser treatment on surface properties of 3Y-TZP for dental applications [thesis]. Ohio: Ohio State University; 2010.
Kukiattrakoon B, Thammasitboon K. The effect of different etching times of acidulated phosphate fluoride gel on the shear bond strength of high-leucite ceramics bonded to composite resin. J Prosthet Dent 2007 Jul;98(1):17-23. doi: 10.1016/S0022-3913(07)60033-X.
Komine F, Kobayashi K, Blatz MB, Fushiki R, Koizuka M, Taguchi K, et al. Durability of bond between an indirect composite veneering material and zirconium dioxide ceramics. Acta Odontol Scand 2013 May-Jul;71(4):457-63. doi: 10.3290/j.jad.a22711.
Cristoforides P, Amaral R, May L, Bottino M, Valandro L. Composite resin to yttria stabilized tetragonal zirconia polycrystal bonding: comparison of repair methods. Oper Dent 2012 May-Jun;37(3):263-71. doi: 10.2341/11-193-L.
Qeblawi DM, Munoz CA, Brewer JD, Monaco EA. The effect of zirconia surface treatment on flexural strength and shear bond strength to a resin cement. J Prosthet Dent 2010 Apr;103(4):210-20. doi: 10.1016/S0022-3913(10)60033-9.
Attia A, Kern M. Long-term resin bonding to zirconia ceramic with a new universal primer. J Prosthet Dent 2011 Nov;106(5):319-27. doi: 10.1016/S0022-3913(11)60137-6.
Gale M, Darvell B. Thermal cycling procedures for laboratory testing of dental restorations. J Dent 1999 Feb;27(2):89-99. doi: 10.1016/s0300-5712(98)00037-2.
Blatz MB, Sadan A, Martin J, Lang B. In vitro evaluation of shear bond strengths of resin to densely-sintered high purity zirconium-oxide ceramic after long-term storage and thermal cycling. J Prosthet Dent 2004 Apr;91(4):356-62. doi: 10.1016/j.prosdent.2004.02.001.
Placido E, Meira JB, Lima RG, Muench A, de Souza RM, Ballester RY. Shear versus micro-shear bond strength test: a finite element stress analysis. Dent Mater 2007 Sep;23(9):1086-92. doi: 10.1016/j.dental.2006.10.002.
Phrukkanon S, Burrow MF, Tyas MJ. Effect of cross-sectional surface area on bond strengths between resin and dentin. Dent Mater 1998 Mar;14(2):120-8. doi: 10.1016/s0109-5641(98)00018-9.
Armstrong S, Geraldeli S, Maia R, Raposo LH, Soares CJ, Yamagawa J. Adhesion to tooth structure: a critical review of "micro" bond strength test methods. Dent Mater 2010 Feb;26(2):e50-62. doi: 10.1016/j.dental.2009.11.155.
Harnirattisai C, Roengrungreang P, Rangsisiripaiboon U, Senawongse P. Shear and micro-shear bond strengths of four self-etching adhesives measured immediately and 24 hours after application. Dent Mater J 2012 Sep;31(5):779-87. doi: 10.4012/dmj.2012-013.
Souza GM, Thompson VP, Braga RR. Effect of metal primers on microtensile bond strength between zirconia and resin cements. J Prosthet Dent. 2011 May;105(11):296-303. doi: 10.1016/S0022-3913(11)60055-3.
Ikemura K, Tanaka H, Fujii T, Deguchi M, Endo T, Kadoma Y. Development of a new single-bottle multi-purpose primer for bonding to dental porcelain, alumina, zirconia, and dental gold alloy. Dent Mater J 2011 Jul;30(4):478-84. doi: 10.4012/dmj.2010-182.
Fonseca RG, Rached FO, Reis JN, Rambaldi E, Baldissara P. Effect of particle size on the flexural strength and phase transformation of an airborne-particle abraded yttria-stabilized tetragonal zirconia polycrystal ceramic. J Prosthet Dent 2013 Dec;110(6):510-4. doi: 10.1016/j.prosdent.2013.07.007.
Koenig V, Vanheusden AJ, Goff SO, Mainjot AK. Clinical risk factors related to failures with zirconia-based restorations: an up to 9-year retrospective study. J Dent 2013 Dec;41(12):1164-74. doi: 10.1016/j.jdent.2013.10.009.
Ozcan M, Valandro LF, Pereira SM, Amaral R, Bottino MA, Pekkan G. Effect of surface conditioning modalities on the repair bond strength of resin composite to the zirconia core/veneering ceramic complex. J Adhes Dent 2013 Jun;15(3):207-10. doi: 10.3290/j.jad.a29717.
Re D, Augusti D, Augusti G, Giovannetti A. Early bond strength to low-pressure sandblasted zirconia: evaluation of a self-adhesive cement. Eur J Esthet Dent 2012 Summer;7(2):164-75.
Papia E, Larsson C, Toit MD, Steyern VV. Bonding between oxide ceramics and adhesive cement systems: a systematic review. J Biomed Mater Res Part B: Appl Biomater 2014 Feb;102(3):395-413. doi: 10.1002/jbm.b.33013.
Koizumi H, Nakayama D, Komine F, Blatz MB, Matsumura H. Bonding of resin-based luting cements to zirconia with and without the use of ceramic priming agents. J Adhes Dent 2012 Aug;14(4):385-92. doi: 10.3290/j.jad.a22711
Sarmento HR, Campos F, Sousa RS, Machado JP, Souza RO, Bottino MA, et al. Influence of air-particle deposition protocols on the surface topography and adhesion of resin cement to zirconia. Acta Odontol Scand 2014 Jul;72(5):346-53. doi: 10.3109/00016357.2013.837958.
Chen L, Shen H, Suh BI. Effect of incorporating BisGMA resin on the bonding properties of silane and zirconia primers. J Prosthet Dent 2013 Nov;110(5):402-7. doi: 10.1016/j.prosdent.2013.04.005.