Calcium Hydroxide improves epoxy sealer adhesion on root dentin

Autores

  • Carlos Henrique Ribeiro Camargo São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Restorative Dentistry – SP – Brazil.
  • Bruna Pastro de Lara São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Restorative Dentistry – SP – Brazil.
  • Gleyce Oliveira Silva São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Restorative Dentistry – SP – Brazil.
  • Noala Vicensoto Moreira Milhan São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Biosciences and Oral Diagnosis – SP – Brazil.
  • Simone Helena Ferreira Gonçalves São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Biosciences and Oral Diagnosis – SP – Brazil.
  • Samira Esteves Afonso Camargo São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Biosciences and Oral Diagnosis – SP – Brazil.

DOI:

https://doi.org/10.14295/bds.2017.v20i2.1400

Resumo

Objective: The aim of this study is to evaluate the adhesion of an endodontic sealer (AHPlus in root canals after the use of different protocols of 17% EDTA and the use of intracanal medication (ICM) based on calcium hydroxide in aqueous vehicle. Material and Methods: For this, 72 single-rooted human teeth were instrumented up to #50 and divided into six groups (n = 12). Group 1: EDTA for 3 min; Group 2: 3 mL of EDTA + 3 min of EDTA; Group 3: 3 mL of EDTA + 3 min of EDTA + 30 seconds of ultrasonic agitation; Group 4: EDTA for 3 min + ICM; Group 5: 3 mL of EDTA + 3 min of EDTA + ICM; Group 6: 3 mL of EDTA + 3 min of EDTA + 30 seconds of ultrasonic agitation + ICM. The root canals were filled with endodontic sealer after each protocol and after 7 days they were prepared to the push-out test. The data were analyzed using ANOVA two factors (p < 0.05). Results: It was observed no statistically difference in bond strength in the 3 different 17% EDTA protocols. However, the use of ICM increased significantly the resistance adhesion. Conclusion: Intracanal medication based on calcium hydroxide improved the bond strength of AHPlus to dentin walls, regardless of the EDTA protocol.

Keywords

Calcium hydroxide; EDTA; Dentin.

Downloads

Não há dados estatísticos.

Downloads

Publicado

2017-06-28

Como Citar

1.
Camargo CHR, de Lara BP, Silva GO, Milhan NVM, Gonçalves SHF, Camargo SEA. Calcium Hydroxide improves epoxy sealer adhesion on root dentin. BDS [Internet]. 28º de junho de 2017 [citado 7º de setembro de 2025];20(2):108-13. Disponível em: https://bds.ict.unesp.br/index.php/cob/article/view/1400

Edição

v. 20 n. 2 (2017): Apr. - Jun. / 2017 - Published Jun 2017

Seção

Artigos de Pesquisa Clínica ou Laboratorial

Licença

TRANSFERÊNCIA DE DIREITOS AUTORAIS E DECLARAÇÃO DE RESPONSABILIDADE



Toda a propriedade de direitos autorais do artigo "____________________________________________________________________" é transferido do autor(es) para a CIÊNCIA ODONTOLÓGICA BRASILEIRA, no caso do trabalho ser publicado. O artigo não foi publicado em outro lugar e não foi submetido simultaneamente para publicação em outra revista.

Vimos por meio deste, atestar que trabalho é original e não apresenta dados manipulados, fraude ou plágio. Fizemos contribuição científica significativa para o estudo e estamos cientes dos dados apresentados e de acordo com a versão final do artigo. Assumimos total responsabilidade pelos aspectos éticos do estudo.



Este texto deve ser impresso e assinado por todos os autores. A versão digitalizada deverá ser apresentada como arquivo suplementar durante o processo de submissão.


Artigos mais lidos pelo mesmo(s) autor(es)