Influence of indirect reinforcements on the flexural strength of a thermally activated acrylic resin used for complete dentures

Autores

  • Jean Soares Miranda São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.
  • Caroline Cotes Marinho Universidade Brasil – São Paulo – SP – Brazil.
  • Vanessa Cruz Macedo São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.
  • Aline Serrado de Pinho Barcellos São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.
  • Thaís Cachuté Paradella São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.
  • Tarcísio José Arruda Paes Jr São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.
  • Estevão Tomomitsu Kimpara São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.

DOI:

https://doi.org/10.14295/bds.2018.v21i2.1539

Resumo

Objetive: This research aimed to verify the performance of thermally activated acrylic resin (TAAR) combined with a mix of glass and aramid fibers and/or composite resin of indirect use by a tree point bending test. Material and Methods: Ten samples, with 65 x 10 x 2.5 mm, were prepared for each group (n = 10): CO, control of only TAAR; CR, in which an 60 mm indirect composite resin was polymerized together with the acrylic resin during the thermo-polymerization cycle; SS, in which ceramic glass mixed with aramid fibers cut 60 mm in length were incorporated into the samples; and SC, in which the same fibers were incorporated with addiction of the indirect composite resin. A three-point flexural strength test was performed with a universal testing machine with a load of 50KgF at a speed of 5 mm/min in the center of the samples supported by a suitable device. The reinforced face was placed to the tensile side. The statistical one-way ANOVA and Tukey tests were made with a significance level of 95%. Results: The mean value for the CO was 60,27 ± 24,18 MPa, for CR it was 38,39±12,75 MPa, for SS it was 79,97±12,75 Mpa and for CS it was 32,40±9,05 MPa. Conclusion: The use of glass and aramid fibers at the base of a TAAR increased the three-point flexural strength, however when indirect composite resin was incorporated, a significant drop of this mechanical property was observed.

 

Keywords

Acrylic resin; Complete denture; Composite resin.

Downloads

Não há dados estatísticos.

Downloads

Publicado

2018-04-19

Como Citar

1.
Miranda JS, Marinho CC, Macedo VC, Barcellos AS de P, Paradella TC, Paes Jr TJA, Kimpara ET. Influence of indirect reinforcements on the flexural strength of a thermally activated acrylic resin used for complete dentures. BDS [Internet]. 19º de abril de 2018 [citado 11º de setembro de 2025];21(2):150-6. Disponível em: https://bds.ict.unesp.br/index.php/cob/article/view/1539

Edição

v. 21 n. 2 (2018): Apr. - Jun. / 2018 - Published April 2018

Seção

Artigos de Pesquisa Clínica ou Laboratorial

Licença

TRANSFERÊNCIA DE DIREITOS AUTORAIS E DECLARAÇÃO DE RESPONSABILIDADE



Toda a propriedade de direitos autorais do artigo "____________________________________________________________________" é transferido do autor(es) para a CIÊNCIA ODONTOLÓGICA BRASILEIRA, no caso do trabalho ser publicado. O artigo não foi publicado em outro lugar e não foi submetido simultaneamente para publicação em outra revista.

Vimos por meio deste, atestar que trabalho é original e não apresenta dados manipulados, fraude ou plágio. Fizemos contribuição científica significativa para o estudo e estamos cientes dos dados apresentados e de acordo com a versão final do artigo. Assumimos total responsabilidade pelos aspectos éticos do estudo.



Este texto deve ser impresso e assinado por todos os autores. A versão digitalizada deverá ser apresentada como arquivo suplementar durante o processo de submissão.


Artigos mais lidos pelo mesmo(s) autor(es)

1 2 > >>